 | This article needs additional citations for verification. Please help improve this article by adding citations to reliable sources. Unsourced material may be challenged and removed. Find sources: "Vicat softening point" – news · newspapers · books · scholar · JSTOR (December 2009) (Learn how and when to remove this message) |
 | The topic of this article may not meet Misplaced Pages's general notability guideline. Please help to demonstrate the notability of the topic by citing reliable secondary sources that are independent of the topic and provide significant coverage of it beyond a mere trivial mention. If notability cannot be shown, the article is likely to be merged, redirected, or deleted. Find sources: "Vicat softening point" – news · newspapers · books · scholar · JSTOR (August 2022) (Learn how and when to remove this message) |
Vicat softening temperature or Vicat hardness is the determination of the softening point for materials that have no definite melting point, such as plastics. It is taken as the temperature at which the specimen is penetrated to a depth of 1 mm by a flat-ended needle with a 1 mm circular or square cross-section. For the Vicat A test, a load of 10 N is used. For the Vicat B test, the load is 50 N. It is named after the French engineer Louis Vicat.
Standards to determine Vicat softening point include ASTM D 1525 and ISO 306, which are largely equivalent.
The vicat softening temperature can be used to compare the heat-characteristics of different materials.
Four different methods may be used for testing.
| Method | Load | Heating rate |
|---|---|---|
| (N) | (°C/h) | |
| A50 | 10 | 50 |
| B50 | 50 | 50 |
| A120 | 10 | 120 |
| B120 | 50 | 120 |
ISO 10350 Note
ISO 10350 Vicat values are tested using the B50 method.
Similar Standards: ASTM D1525